Explore the alloy composition of QC-10 aluminum alloy

QC-10 aluminum alloy has greater strength, higher stability and more reliable durability. The following is a further explanation of the characteristics of QC-10 aluminum alloy:

QC-10 chemical composition:

Cu: 0.15-0.4

Si: 0.4-0.8 ,

Fe: 0.7-,0.13

Mn0.15-0.50,

Mg: 0.8-1.2

Zn: 0.25- 0.50

Cr: 0.04-0.35

Ti: 0.15

Density is 2.72g/cm3

Mechanical properties:

Tensile strength (25°CMPa)

Yield strength (25°CMPa)

Hardness 500kg force 10mm ball

Elongation 1.6mm (1 /16in) thickness

Note: The longitudinal mechanical properties of the pipe at room temperature

Different properties in different states.

High strength: After improvements in alloy composition, QC-10 aluminum alloy has greater strength. This allows it to withstand greater loads and cope with harsher working environments. High strength is important for applications where structural integrity and stability need to be maintained.

High stability: QC-10 aluminum alloy also improves its stability during the process of improving the alloy composition. Stability refers to the performance of a material under different temperatures and environmental conditions. QC-10 aluminum alloy with high stability can better adapt to different working environments and maintain the consistency of its performance.

Reliable durability: The improved QC-10 aluminum alloy has more reliable durability. Durability refers to the ability of a material to maintain its performance over time and under repeated stress. The higher durability enables QC-10 aluminum alloy to maintain stable performance during long-term use and extend its service life.