Alumold-600 aluminum alloy wear-resistant and impact-resistant thermoforming mold material

Alumold-600 aluminum alloy is an aluminum alloy material suitable for super-hard mold and thick plate applications.

Chemical composition of Alumold-600:

Cu: 0.15-0.4

Si: 0.4-0.8,

Fe: 0.7-, 0.13

Mn0.15-0.50,

Mg: 0.8-1.2

Zn: 0.25-0.50

Cr: 0.04-0.35

Ti: 0.15

Density is 2.72g/cm3

Mechanical properties:

Tensile strength (25°CMPa)

p>

Yield strength (25°CMPa)

Hardness 500kg force 10mm ball

Elongation 1.6mm (1/16in) thickness

Note: Longitudinal mechanical properties of pipes at room temperature

Different properties in different states.

Alumold-600 aluminum alloy has very strong hardness and strength properties, making it ideal for manufacturing ultra-hard molds and thick plates that can withstand high loads. Its high strength and hardness properties ensure the material's durability and reliability during use. As an injection mold material, Alumold-600 aluminum alloy can withstand the high pressure and friction generated during the injection molding process and has good wear resistance.

At the same time, for the demand for large loading tools, the high strength and hardness properties of Alumold-600 aluminum alloy enable it to withstand heavy loads and the challenges brought by various transportation applications.

In general, Alumold-600 aluminum alloy is an aluminum alloy material with high strength, hardness and wear resistance, especially suitable for manufacturing super-hard molds and thick plates used to withstand high loads. . It ensures the stability and durability of molds and loading tools in use.